Korundtelliste tulekindlad omadused
As shown in the Al2O3-Cr2O3 binary phase diagram, Al2O3 and Cr2O3 can form a continuous solid solution without the formation of eutectic. Therefore, adding Cr2O3 to high-purity corundum materials, regardless of the amount added, not only does not reduce the material's refractory properties, but actually improves them. The refractoriness (>1790 ℃) and load softening temperature (>1700 kraadi) kroomkorundtellised on paremad kui kõrge-puhtusastmega korundtoodete omad.
Korund telliste tugevus
The room temperature compressive strength of high-purity corundum bricks is generally 70–100 MPa, while the room temperature compressive strength of high-performance chromium corundum bricks is generally >150 MPa, mis on oluliselt kõrgem kui tavalistel korundtellistel. Selle põhjuseks on asjaolu, et põletamise käigus tekivad Al2O3-Cr2O3 tahked lahused osakeste, osakeste ja peenpulbrite ning peenpulbrite endi vahel. Need tahked lahused toimivad nagu sillad, ühendades osakesed ja peened pulbrid, suurendades oluliselt materjali tugevust.
Termošoki stabiilsus
Aruannete kohaselt väheneb Cr2O3 lisamisel korundile termilise šoki stabiilsus Cr2O3 sisalduse suurenemisega, eriti kui Cr2O3 sisaldus on vahemikus 10% kuni 66%. Teisisõnu on madala Cr2O3 sisaldusega kroomkorundtellistel parem termilise šoki stabiilsus kui kõrge Cr2O3 sisaldusega tellistel.
Räbu erosioonikindlus
Erinevate tulekindlate oksiidide lahustuvus sulasöe räbus: Cr2O3 lahustuvus kivisöe gaasistamise räbus (SiO2-CaO süsteem) ja erinevates klaasisulates on palju madalam kui teistel oksiidmaterjalidel. Seetõttu on Cr2O3 või Cr2O3 sisaldavatel tulekindlatel materjalidel hea vastupidavus korrosioonile terasräbu, värvilise metalli sulatusräbu, kivisöe gaasistamisräbu, naftagaasistamise räbu ja erinevate klaasisulamite suhtes.